The crystal structures of PdBi modifications from in-situ high-temperature single-crystal X-ray diffraction

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The transformation of PdBi compound at high temperatures was studied using in-situ high-temperature single-crystal X-ray diffraction. The new data about crystal structure of high temperature PdBi modification is obtained. The structure of PdBi at T = 293, 373, 423 and 473 К, is orthorhombic, space group Cmc21, unit cell parameters: a = 8.7160(3), b = 7.2031(3), c = 10.6631(4) Å, V = 669.45(4) Å3, Z = 16 (293 К). Upon further heating, a phase transition to the high-temperature modification occurs. The structure of PdBi at T = 523 and 573 К was solved in orthorhombic space group Cmcm, a = 3.6162(3), b = 10.6446(8), c = 4.4208(4) Å, V = 170.17(3) Å3, Z = 4 (523 К).

Толық мәтін

Рұқсат жабық

Авторлар туралы

O. Кarimova

Institute of Geology of Ore Deposits RAS

Хат алмасуға жауапты Автор.
Email: oxana.karimova@gmail.com
Ресей, Moscow

A. Zolotarev

St. Petersburg State University

Email: oxana.karimova@gmail.com

Institute of Earth Sciences, St. Petersburg State University

Ресей, St. Petersburg

A. Mezhueva

Institute of Geology of Ore Deposits RAS

Email: oxana.karimova@gmail.com
Ресей, Moscow

L. Ivanova

Institute of Geology of Ore Deposits RAS

Email: oxana.karimova@gmail.com
Ресей, Moscow

D. Chareev

Institute of Experimental Mineralogy RAS; Ural Federal University; Dubna State University

Email: oxana.karimova@gmail.com
Ресей, Moscow region, Chernogolovka; Ekaterinburg; Moscow region, Dubna

Әдебиет тізімі

  1. Алексеевский Н.Е. // ЖЭТФ. 1952. Т. 23. С. 484.
  2. Журавлев Н.Н., Жданов Г.С. // ЖЭТФ. 1953. Т. 25. С. 485.
  3. Хейкер Д.М., Жданов Г.С., Журавлев Н.Н. // ЖЭТФ. 1953. Т. 25. № 5. С. 621.
  4. Bahtt Y.C., Schubert K. // J. Less-Comon. Met. 1979. V. 64. P. P17. https://doi.org/10.1016/0022-5088(79)90184-X
  5. Ионов В.М., Томилин Н.А., Прозоровский А.Е. и др. // Кристаллография. 1989. Т. 34. № 4. С. 829.
  6. Okamoto H. // J. Phase Equilibria. 1994. V. 15. № 2. P. 191. https://doi.org/10.1007/BF02646366
  7. Rigaku Oxford Diffraction, CrysAlisPro Software System, version 41.104a. Rigaku Oxford Diffraction, Yarnton, England, 2021.
  8. Sheldrick G.M. // Acta Cryst. A. 2015. V. 71. P. 3. https://doi.org/10.1107/S2053273314026370
  9. Sheldrick G.M. // Acta Cryst. C. 2015. V. 71. P. 3. https://dx.doi.org/10.1107/S2053229614024218
  10. Farrugia L.J. // J. Appl. Cryst. 1999. V. 32. P. 837. https://doi.org/10.1107/S0021889899006020
  11. Pennington W.T. // J. Appl. Cryst. 1999. V. 32. P. 1028. https://doi.org/10.1107/S0021889899011486
  12. Cambridge Crystallographic Data Centre (CCDC). Inorganic Crystal Structure Data Base – ICSD. https://www.ccdc.cam.ac.uk/, http://www.fizkarlsruhe.de
  13. Бюргер М.Дж. // Кристаллография. 1971. Т. 16. С. 1084.
  14. Филатов С.К., Пауфлер П. // Зап. Рос. минерал. о-ва. 2019. Т. 148. № 5. С. 1.

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу
2. Fig. 1. SEM image of a PdBi crystal obtained in the backscattered electron detection mode.

Жүктеу (128KB)
Метадеректер
3. Fig. 2. Coordination polyhedra of palladium in the structure of the β-modification of PdBi.

Жүктеу (412KB)
Метадеректер
4. Fig. 3. Projection of the crystal structure of β-PdBi onto the plane: a – (101), b – (011).

Жүктеу (349KB)
Метадеректер
5. Fig. 4. Coordination polyhedron of palladium in the structure of the γ-modification of PdBi.

Жүктеу (212KB)
Метадеректер
6. Fig. 5. Projection of the crystal structure of γ-PdBi onto the plane: a – (101), b – (011).

Жүктеу (136KB)
Метадеректер
7. Fig. 6. Schematic representation of chains of palladium atoms in the structure of the PdBi compound at different temperatures, changes in the lengths of Pd–Pd bonds and the angles between them in the process of converting β-PdBi (293 and 473 K) into γ-PdBi (573 K).

Жүктеу (134KB)
Метадеректер

© Russian Academy of Sciences, 2025